<p>The article discusses the static and dynamic properties of high-strength, boron-containing Hardox 600 steel that is resistant to abrasive wear, both in its delivery state and after normalization. Since the available published material in the literature does not have any real mechanical indicators of the abovementioned steel, a static tension test was carried out at an ambient temperature. The steel’s tensile strength, yield strength, Young’s modulus, elongation and reduction of area were determined from the test. The Charpy impact test at temperatures of −40 °C, −20 °C, 0 °C, and +20 °C and fractographic analysis were performed to determine the transition temperature of ductility to brittleness. In dynamic load conditions, the assigned values of impact energy do not always truly determine the material behavior. Thus, the aim of the fractography was to provide precision when determining the behavior. A significant difference in the impact energy of the tested steel with respect to its heat treatment and ductile-brittle transition temperature was observed and determined based on the impact test result, as well as the nature of the fracture. On the basis of the determined structural and strength characteristics, an analysis of the possibility of application of Hardox 600 steel on selected elements of working machines was performed.</p>
</abstract>

The article discusses the static and dynamic properties of high-strength, boron-containing Hardox 600 steel that is resistant to abrasive wear, both in its delivery state and after normalization. Since the available published material in the literature does not have any real mechanical indicators of the abovementioned steel, a static tension test was carried out at an ambient temperature. The steel’s tensile strength, yield strength, Young’s modulus, elongation and reduction of area were determined from the test. The Charpy impact test at temperatures of −40 °C, −20 °C, 0 °C, and +20 °C and fractographic analysis were performed to determine the transition temperature of ductility to brittleness. In dynamic load conditions, the assigned values of impact energy do not always truly determine the material behavior. Thus, the aim of the fractography was to provide precision when determining the behavior. A significant difference in the impact energy of the tested steel with respect to its heat treatment and ductile-brittle transition temperature was observed and determined based on the impact test result, as well as the nature of the fracture. On the basis of the determined structural and strength characteristics, an analysis of the possibility of application of Hardox 600 steel on selected elements of working machines was performed.

Analysis of the static and dynamic properties of wear-resistant Hardox 600 steel in the context of its application in working elements

Wroclaw University of Science and Technology

Materials Science-Poland

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.

The article discusses the static and dynamic properties of high-strength, boron-containing Hardox 600 steel that is resistant to abrasive wear, both in its...

Analysis of the static and dynamic properties of wear-resistant Hardox 600 steel in the context of its application in working elements

Published Online: Jul 06, 2021

Page range: 86 - 102

Received: Mar 27, 2021

Accepted: Mar 27, 2021

DOI: https://doi.org/10.2478/msp-2021-0007

Keywords
martensitic boron steel, steel resistant to abrasive wear, mechanical properties, structures, ductile to brittle transition temperature, fractographic analysis

© 2021 Ł. Konat et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.

Analysis of the static and dynamic properties of wear-resistant Hardox 600 steel in the context of its application in working elements

Published Online: Jul 06, 2021

Page range: 86 - 102

Received: Mar 27, 2021

Accepted: Mar 27, 2021

DOI: https://doi.org/10.2478/msp-2021-0007

Keywordsmartensitic boron steel, steel resistant to abrasive wear, mechanical properties, structures, ductile to brittle transition temperature, fractographic analysis

© 2021 Ł. Konat et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.

Keywords
martensitic boron steel, steel resistant to abrasive wear, mechanical properties, structures, ductile to brittle transition temperature, fractographic analysis