Effect of the electrodeposition potential on the magnetic properties of FeCoNi films

Published Online: 18 Oct 2019
Volume & Issue: Volume 37 (2019) - Issue 3 (September 2019)
Page range: 389 - 394
Received: 07 Apr 2018
Accepted: 12 Nov 2018
Journal Details
License
Format
Journal
eISSN
2083-134X
First Published
16 Apr 2011
Publication timeframe
4 times per year
Languages
English
Abstract

The effect of electrodeposition potential on the magnetic properties of the FeCoNi films has been reported in this paper. The FeCoNi electrodeposition was carried out from sulfate solution using potentiostatic technique. The obtained FeCoNi films were characterized by X-ray diffractometer (XRD), atomic absorption spectrometer (AAS) and vibrating sample magnetometer (VSM). It has been shown that the electrodeposition potential applied during the synthesis process determines the magnetic characteristics of FeCoNi films. The more negative potential is applied, the higher Ni content is in the FeCoNi alloy. At the same time, Co and Fe showed almost similar trend in which the content decreased with an increase in applied potential. The mean crystallite size of FeCoNi films was ranging from 11 nm to 15 nm. VSM evaluation indicated that the FeCoNi film is a ferromagnetic alloy with magnetic anisotropy. The high saturation magnetization of FeCoNi film was ranging from 86 A·m2/kg to 105 A·m2/kg. The film is a soft magnetic material which was revealed by a very low coercivity value in the range of 1.3 kA/m to 3.7 kA/m. Both the saturation magnetization and coercivity values decreased at a more negative electrodeposition potential.

Keywords

[1] Osaka T., Takai M., Hayashi K., Ohashi K., Nature, 392 (1998), 796.10.1038/33888Search in Google Scholar

[2] Luciu I., Duday D., Choquet P., Perigo E.A., Michels A., Wirtz T., Appl. Surf. Sci., 389 (2016), 578.10.1016/j.apsusc.2016.07.126Search in Google Scholar

[3] Pikula T., Oleszak D., Marek P., J. Magn. Magn. Mater., 320 (2008), 413.10.1016/j.jmmm.2007.06.020Search in Google Scholar

[4] Fu P., Chen G., Xu Y., Cai P., Wang X.H., Mater. Sci.-Poland, 30 (2012), 259.10.2478/s13536-012-0031-2Search in Google Scholar

[5] Raanaei H., Eskandari H., Mohammad-Hosseini V., J. Magn. Magn. Mater., 398 (2016), 190.10.1016/j.jmmm.2015.09.031Search in Google Scholar

[6] Baghbaderani H.A., Shara S., Chermahini M.D., Powder Technol., 230 (2012), 241.10.1016/j.powtec.2012.07.039Search in Google Scholar

[7] Shakya P., Cox B., Davis D., J. Magn. Magn. Mater., 324 (2012), 453.10.1016/j.jmmm.2011.08.023Search in Google Scholar

[8] Duan Y., Zhang Y., Wang T., Gu S., Xin L., Xingzun L.V., Mater. Sci. Eng. B-Adv., 185 (2014), 86.Search in Google Scholar

[9] Ali G.A.M., Yusoff M.M., Ng Y.H., Lim H.N., Chong K.F., Curr. Appl. Phys., 15 (2015), 1143.10.1016/j.cap.2015.06.022Search in Google Scholar

[10] Daud A.r., Budi S., Radiman S., Sains Malaysiana, 40 (2011), 1019.Search in Google Scholar

[11] Hanafi I., Daud A.R., Radiman S., Gani M.H.A., Budi S., J. Phys. Conf. Ser., 431 (2013), 1.10.1088/1742-6596/431/1/012013Search in Google Scholar

[12] Hanafi I., Daud A.R., Radiman S., Port. Electrochim. Acta, 35 (2017), 1.10.4152/pea.201701001Search in Google Scholar

[13] Talik E., Guzik A., Zajdel P., Lipińska L., Baran M., Szubka M., Mater. Res. Bull., 83 (2016), 56.10.1016/j.materresbull.2016.05.018Search in Google Scholar

[14] Akbulut S., Akbulut A., Özdemir M., Yildiz F., J. Magn. Magn. Mater., 390 (2015), 137.10.1016/j.jmmm.2015.04.061Search in Google Scholar

[15] Budi S., Hafizah M.e., Manaf A., AIP, 1746 (2016), 020012-1.Search in Google Scholar

[16] Budi S., Kurniawan B., Mott D.M., Maenosono S., Umar A.A., Manaf A., Thin Solid Films, 642 (2017), 51.10.1016/j.tsf.2017.09.017Search in Google Scholar

[17] Xiao L., Chen Z., Feng C., Liu L., Bai Z.-Q., Wang Y., Qian L., Zhang Y., Li Q., Jiang K., Fan S., Nano Lett., 8 (2008), 4539.10.1021/nl802750z19367976Search in Google Scholar

[18] Lee H., Wang L., Bain J.A., Laughlin D.E., IEEE T. Magn., 41 (2005), 654.10.1109/TMAG.2004.838041Search in Google Scholar

[19] Budi S., Daud A.R., Radiman S., Umar A.A., Appl. Surf. Sci., 257 (2010), 1027.10.1016/j.apsusc.2010.07.103Search in Google Scholar

[20] Matlosz M., J. Electrochem. Soc., 140 (1993), 2272.10.1149/1.2220807Search in Google Scholar

[21] Grazulis S., Chateigner D., Downs R.T., Yokochi A.F.T., Quirós M., Lutterotti L., Manakova E., Butkus J., Moeck P., Le Bail A., J. Appl. Crystallogr., 42 (2009), 726.10.1107/S0021889809016690325373022477773Open DOISearch in Google Scholar

[22] Veith M., Bubel C., Zimmer M., Dalt. Trans., 40 (2011), 6028.10.1039/c1dt10067j21541390Search in Google Scholar

[23] Dolati A., Sababi M., Nouri E., Ghorbani M., Mater. Chem. Phys., 102 (2007), 118.10.1016/j.matchemphys.2006.07.009Search in Google Scholar

[24] Yang Y., Int. J. Electrochem. Sci., 10 (2015), 5164.Search in Google Scholar

[25] Cullity B.D., Graham C.D., Introduction to Magnetic Materials, John Wiley & Sons, New Jersey, 2008.10.1002/9780470386323Search in Google Scholar

[26] Veligatla M., Katakam S., Das S., Dahotre N., Gopalan R., Prabhu D., Babu D.A., Choi-Yim H., Mukherjee S., Metall. Mater. Trans., A 46 (2015), 1019.10.1007/s11661-014-2714-2Search in Google Scholar

Recommended articles from Trend MD

Plan your remote conference with Sciendo