<abstract xmlns="http://www.w3.org/1999/xhtml">The Brayton cycle with supercritical carbon dioxide is considered as an innovative technology with the potential to replace conventional steam cycles. The optimization of the supercritical CO2 cycle (sCO2) is necessary and important to achieve the required thermal cycle parameters. The above optimization focuses on the setting of the energy cycle as such, the design solution of the individual components and, the last but not least, on the selection of suitable construction materials. Due to the operating conditions, namely temperatures exceeding 550 °C and pressure up to 25 MPa, material research is one of the important areas of the research and development of sCO2 energy cycles. Construction materials for sCO2 power cycle equipment include HR6W, T92 and Haynes HR235 alloys. This work presents results of the corrosion test, in which samples of these materials were exposed to sCO2 at 550 °C and 25 MPa for 1000 hours. Corrosion after exposure was examined using a light optical microscope (LOM) and a scanning electron microscope (SEM). The significant differences in corrosion attack between the investigated materials and the formation of a protective oxide layer on the surface were observed.</abstract>

The Brayton cycle with supercritical carbon dioxide is considered as an innovative technology with the potential to replace conventional steam cycles. The optimization of the supercritical CO2 cycle (sCO2) is necessary and important to achieve the required thermal cycle parameters. The above optimization focuses on the setting of the energy cycle as such, the design solution of the individual components and, the last but not least, on the selection of suitable construction materials. Due to the operating conditions, namely temperatures exceeding 550 °C and pressure up to 25 MPa, material research is one of the important areas of the research and development of sCO2 energy cycles. Construction materials for sCO2 power cycle equipment include HR6W, T92 and Haynes HR235 alloys. This work presents results of the corrosion test, in which samples of these materials were exposed to sCO2 at 550 °C and 25 MPa for 1000 hours. Corrosion after exposure was examined using a light optical microscope (LOM) and a scanning electron microscope (SEM). The significant differences in corrosion attack between the investigated materials and the formation of a protective oxide layer on the surface were observed.

Evaluation of microstructure of the steels after exposure in supercritical CO2

KOM – Corrosion and Material Protection Journal

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.

Evaluation of microstructure of the steels after exposure in supercritical CO

The Brayton cycle with supercritical carbon dioxide is considered as an innovative technology with the potential to replace conventional steam cycles. The...

Evaluation of microstructure of the steels after exposure in supercritical CO₂

Published Online: Dec 31, 2020

Page range: 108 - 115

DOI: https://doi.org/10.2478/kom-2020-0016