Enhancing Mechanical Properties of Clay Brick by Using Stone Powder

Hundreds of studies have been written in the last several decades on the advantages of using stone powder as a raw material in the production of fired clay bricks. The durability and long-term behavior of the finished product, however, have received very little attention in the literature. Clay bricks are generally fired at high temperatures in developing countries, which reduces the mechanical performance of the bricks. This is especially evident in extreme environmental settings where weathering leads to significant damage. The evaluation of concrete waste (stone powder) used to make fired clay bricks is the main topic of this study. There are two sections: the first evaluates how adding stone powder to clay bricks improves their physical characteristics such absorption, efflorescence, density, and firing shrinkage. The impact of stone powder on the mechanical characteristics of specimens of burned clay bricks, such as compressive and flexural strengths, is covered in the second section. The percentages of stone powder in the clay bricks are 0 %, 5 %, 10 %, 15 %, and 20%. While the ratio of dry soil to water content remains is 0.3. In this work three fire phases are used untel to the maximum temperature is reached. The first one is 300 °C, the second phase is 600 °C, and 900 °C for the third phase. The water absorption of specimens decreased as the quantity of stone powder increased, and efflorescence also decreased, according to the results for the physical attributes. The density does, however, somewhat rise with the amount of stone powder. Additionally, when the amount of stone powder was increased, the experimental results indicated that firing shrinkage decreased. Mechanically considered, clay brick specimens with 20% more stone powder showed stronger compressive flexural capabilities.