<p>In this research, the effect copper on the structural, morphological, optical, and electrical properties of nickel oxide thin films was studied at different copper concentrations. Thin transparent films of nickel oxide (NiO) doped with copper (Cu) were deposited on glass substrates at a temperature of 400 °C using the spray pyrolysis technique. The structural study showed that all the prepared polycrystalline films had a cubic structure with a preferential orientation along (111). Copper was well integrated into the host lattice without changing the structure. SEM images showed that the films were well adhered with a wrinkled network structure. The optical band gap ranges from 3.70 eV to 3.50 eV, and the Urbach energy, which ranges from 0.34 eV to 0.5 eV, has also been discussed. The highest conductivity value of 6.23 × 10⁻³ (Ω·cm)⁻¹ was found at a copper concentration of 2 %.</p>
</abstract>

In this research, the effect copper on the structural, morphological, optical, and electrical properties of nickel oxide thin films was studied at different copper concentrations. Thin transparent films of nickel oxide (NiO) doped with copper (Cu) were deposited on glass substrates at a temperature of 400 °C using the spray pyrolysis technique. The structural study showed that all the prepared polycrystalline films had a cubic structure with a preferential orientation along (111). Copper was well integrated into the host lattice without changing the structure. SEM images showed that the films were well adhered with a wrinkled network structure. The optical band gap ranges from 3.70 eV to 3.50 eV, and the Urbach energy, which ranges from 0.34 eV to 0.5 eV, has also been discussed. The highest conductivity value of 6.23 × 10⁻³ (Ω·cm)⁻¹ was found at a copper concentration of 2 %.

Synthesis and Characterization of Un-Doped and Copper Doped Nickel Oxide Thin Films

Material Sciences Department, Faculty of Science

Metallurgy Department, Engineering Faculty

Annals of West University of Timisoara - Physics

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.

In this research, the effect copper on the structural, morphological, optical, and electrical properties of nickel oxide thin films was studied at different...

Synthesis and Characterization of Un-Doped and Copper Doped Nickel Oxide Thin Films

Published Online: Jul 19, 2024

Page range: -

Received: Mar 18, 2024

Accepted: Jul 08, 2024

DOI: https://doi.org/10.2478/awutp-2024-0014

Keywords
Thin Films, Metal Oxides, NiO, Pyrolysis spray

© 2024 Saliha Bouaicha et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.

Synthesis and Characterization of Un-Doped and Copper Doped Nickel Oxide Thin Films

Published Online: Jul 19, 2024

Page range: -

Received: Mar 18, 2024

Accepted: Jul 08, 2024

DOI: https://doi.org/10.2478/awutp-2024-0014

KeywordsThin Films, Metal Oxides, NiO, Pyrolysis spray

© 2024 Saliha Bouaicha et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.

Keywords
Thin Films, Metal Oxides, NiO, Pyrolysis spray