WaterLase group | Tungsten carbide | |||
---|---|---|---|---|
Median | 95% CI | Median | 95% CI | |
Depth | 166.3 | (86.6–263.1) | 17.6 |
(10.5–28.9) |
WaterLase group | Sound enamel | Only composite | ||
---|---|---|---|---|
Median | 95% CI | Value | Value | |
C K | 14.84 | (11.48–31.51) | 28.46 | 38.17 |
O K | 64.64 | (47.04–68.25) | 57.08 | 44.13 |
Na K | 0.20 | (0.00–0.58) | 0.38 | 0.00 |
P K | 7.76 | (7.22–8.74) | 5.75 |
0.00 |
Cl K | 0.00 | (0.00–0.18) | 0.13 | 0.00 |
Ca K | 11.38 | (9.70–13.14) | 7.76 |
0.00 |
F K | 0.00 | (0.00–0.00) | 0.00 | 2.01 |
Si K | 0.00 | (0.00–0.00) | 0.00 | 11.47 |
Br L | 0.00 | (0.00–0.00) | 0.00 | 1.64 |
Ba L | 0.00 | (0.00–0.00) | 0.00 | 2.58 |
Zr L | 0.48 | (0.00–0.69) | 0.44 | 0.00 |
GROUP | ||||
---|---|---|---|---|
Total | Waterlase (WL) | Tungsten carbide (TC) | ||
Depth in Micrometers | N | 20 | 10 | 10 |
Mean | 96.83 | 173.12 | 20.54 | |
Standard Deviation | 94.90 | 77.40 | 9.40 | |
Minimum | 9.62 | 76.37 | 9.62 | |
Maximum | 285.23 | 285.23 | 37.69 | |
Median | 57.03 | 166.31 | 17.62 |