<abstract xmlns="http://www.w3.org/1999/xhtml">Four different magnetic Fe3O4 nanoparticles were synthesized and characterized by solvothermal method based on different sodium salts. Sodium salts which were used to synthesize the nanoparticles were NaOAc, Na2CO3, a mixture of NaOAc and Na3Cit, and a mixture of NaOAc and Na2C2O4. The structural and optical properties of the synthesized nanoparticles were examined by XRF, XRD, SEM and FT-IR. The results estimated from XRD pattern and SEM image indicated that the second sample (Na2CO3) had the lowest average particle and crystallite size around 29 nm and 43 nm. It was also shown that the first (NaOAc) and second (Na2CO3) samples had the best FT-IR spectra, similar to the available commercial sample which was provided by Merck. At last, the prepared Fe3O4 nanoparticles were applied as sorbents to sorb uranium ions (U(VI)) from radioactive wastewater. The adsorption results showed that the highest U(VI) adsorption was obtained for the second sample in the solution with pH around 10.</abstract>

Four different magnetic Fe3O4 nanoparticles were synthesized and characterized by solvothermal method based on different sodium salts. Sodium salts which were used to synthesize the nanoparticles were NaOAc, Na2CO3, a mixture of NaOAc and Na3Cit, and a mixture of NaOAc and Na2C2O4. The structural and optical properties of the synthesized nanoparticles were examined by XRF, XRD, SEM and FT-IR. The results estimated from XRD pattern and SEM image indicated that the second sample (Na2CO3) had the lowest average particle and crystallite size around 29 nm and 43 nm. It was also shown that the first (NaOAc) and second (Na2CO3) samples had the best FT-IR spectra, similar to the available commercial sample which was provided by Merck. At last, the prepared Fe3O4 nanoparticles were applied as sorbents to sorb uranium ions (U(VI)) from radioactive wastewater. The adsorption results showed that the highest U(VI) adsorption was obtained for the second sample in the solution with pH around 10.

Solvothermal synthesis and characterization of magnetic Fe3O4 nanoparticle by different sodium salt sources

Materials Science-Poland

This article is distributed under the terms of the Creative Commons Attribution Non-Commercial License, which permits unrestricted non-commercial use, distribution, and reproduction in any medium, provided the original work is properly cited.

Solvothermal synthesis and characterization of magnetic FeO nanoparticle by different sodium salt sources

Four different magnetic Fe3O4 nanoparticles were synthesized and characterized by solvothermal method based on different sodium salts. Sodium salts which were...

Solvothermal synthesis and characterization of magnetic Fe₃O₄ nanoparticle by different sodium salt sources

Published Online: Feb 24, 2017

Page range: 50 - 57

Received: Apr 10, 2016

Accepted: Nov 18, 2016

DOI: https://doi.org/10.1515/msp-2017-0004

Keywords
magnetic FeO nanoparticle, solvothermal synthesis, sodium salt sources, uranium adsorption

© 2017 M. Jamshidiyan, A.S. Shirani, GH. Alahyarizadeh

This article is distributed under the terms of the Creative Commons Attribution Non-Commercial License, which permits unrestricted non-commercial use, distribution, and reproduction in any medium, provided the original work is properly cited.

Solvothermal synthesis and characterization of magnetic Fe3O4 nanoparticle by different sodium salt sources

Published Online: Feb 24, 2017

Page range: 50 - 57

Received: Apr 10, 2016

Accepted: Nov 18, 2016

DOI: https://doi.org/10.1515/msp-2017-0004

Keywordsmagnetic FeO nanoparticle, solvothermal synthesis, sodium salt sources, uranium adsorption

© 2017 M. Jamshidiyan, A.S. Shirani, GH. Alahyarizadeh

This article is distributed under the terms of the Creative Commons Attribution Non-Commercial License, which permits unrestricted non-commercial use, distribution, and reproduction in any medium, provided the original work is properly cited.

Solvothermal synthesis and characterization of magnetic Fe₃O₄ nanoparticle by different sodium salt sources

Keywords
magnetic FeO nanoparticle, solvothermal synthesis, sodium salt sources, uranium adsorption