<abstract xmlns="http://www.w3.org/1999/xhtml"><p>The article is aimed at evaluation of chosen properties of thermally sprayed coatings based on tungsten carbide. It was evaluated two types of coatings – WC-FeCrAl and WC-WB-Co. The coatings were deposited on basic material steel AISI 316L. The aim of experimental works was to determine the quality and resistance of coatings in corrosion environment depending on number of thermal cycles. The quality of coatings was evaluated by determination of their adhesion depending on thermal cycles, determination of microhardness and indentation fracture toughness. Coatings were exposed in tribo-corrosion conditions with the presence of 1% NaCl. The results of experimental showed a higher quality of coating WC-WB-Co.</p></abstract>

The article is aimed at evaluation of chosen properties of thermally sprayed coatings based on tungsten carbide. It was evaluated two types of coatings – WC-FeCrAl and WC-WB-Co. The coatings were deposited on basic material steel AISI 316L. The aim of experimental works was to determine the quality and resistance of coatings in corrosion environment depending on number of thermal cycles. The quality of coatings was evaluated by determination of their adhesion depending on thermal cycles, determination of microhardness and indentation fracture toughness. Coatings were exposed in tribo-corrosion conditions with the presence of 1% NaCl. The results of experimental showed a higher quality of coating WC-WB-Co.

Determination of selected properties and fracture toughness of HVOF coatings

Koroze a ochrana materiálu

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

{"article-title":"Determination of selected properties and fracture toughness of HVOF coatings"}

The article is aimed at evaluation of chosen properties of thermally sprayed coatings based on tungsten carbide. It was evaluated two types of coatings –...

Determination of selected properties and fracture toughness of HVOF coatings

Published Online: Dec 30, 2016

Page range: 148 - 153

DOI: https://doi.org/10.1515/kom-2016-0024

© 2016 Landová M. et al., published by De Gruyter Open

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.