Two series of novel thermoplastic poly(carbonate-urethane) elastomers, with different hard-segment content (30 - 60 wt %), were synthesized by melt polymerization from poly(hexane-1,6-diyl carbonate) diol of Mn = 2000 as a soft segment, 4,4'-diphenylmethane diisocyanate (MDI) or hexane-1,6-diyl diisocyanate (HDI) and 6,6'-[methylenebis(1,4-phenylenemethylenethio)]dihexan-1-ol as a chain extender. The structure and basic properties of the polymers were examined by Fourier transform infrared spectroscopy, X-ray diffraction analysis, atomic force microscopy, differential scanning calorimetry, thermogravimetric analysis, Shore hardness and tensile tests. The resulting TPUs were colorless polymers, showing almost amorphous structures. The MDI-based TPUs showed higher tensile strengths (up to 21.3 MPa vs. 15.8 MPa) and elongations at break (up to 550% vs. 425%), but poorer low-temperature properties than the HDI-based analogs.