<p>This study is to identify the most important control elements that will result in improve the tensile strength of Laser Beam Welded Cu-Ni 90/10 alloy joints. The different laser welding process parameters and levels were used for  joining of Cu-Ni alloy. The process parameters like Laser Power (LP), Shielding Gas (argon) (SG), Focal Position (FP), &amp; Welding Speed (WS) were chosen in the experimental study. The welding was carried on 4mm thick plate as per Taguchi’s experimental design. The mechanical properties were evaluated and microstructural observations were carried out. It was discovered that highest tensile strength of 234 MPa &amp; hardness of 83 Hv were obtained which has 90 % and 87 % of the base material. The most influential optimal process parameters were determined using S/N analysis and the percentage contribution of each process parameter was estimated using ANOVA. It was found that laser power was influential parameter with a 64 % contribution in obtaining highest strength of laser welded joints. The experimental values and the results of the confirmation experiments were in good agreement.</p>
</abstract>

This study is to identify the most important control elements that will result in improve the tensile strength of Laser Beam Welded Cu-Ni 90/10 alloy joints. The different laser welding process parameters and levels were used for  joining of Cu-Ni alloy. The process parameters like Laser Power (LP), Shielding Gas (argon) (SG), Focal Position (FP), & Welding Speed (WS) were chosen in the experimental study. The welding was carried on 4mm thick plate as per Taguchi’s experimental design. The mechanical properties were evaluated and microstructural observations were carried out. It was discovered that highest tensile strength of 234 MPa & hardness of 83 Hv were obtained which has 90 % and 87 % of the base material. The most influential optimal process parameters were determined using S/N analysis and the percentage contribution of each process parameter was estimated using ANOVA. It was found that laser power was influential parameter with a 64 % contribution in obtaining highest strength of laser welded joints. The experimental values and the results of the confirmation experiments were in good agreement.

Optimization of Laser Beam Welding Parameters for 90/10 Cupronickel Alloy Welds Using Taguchi Method

Strojnícky časopis - Journal of Mechanical Engineering

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

This study is to identify the most important control elements that will result in improve the tensile strength of Laser Beam Welded Cu-Ni 90/10 alloy joints....

Optimization of Laser Beam Welding Parameters for 90/10 Cupronickel Alloy Welds Using Taguchi Method

Online veröffentlicht: 09. Mai 2022

Seitenbereich: 89 - 98

DOI: https://doi.org/10.2478/scjme-2022-0009

Schlüsselwörter
Laser beam welding (LBM), Copper–nickel (Cu–Ni) 90/10 alloys, Tensile strength (TS), Hardness, Design matrix and Taguchi method

© 2022 Maddili Praveena Chakravarthy et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Optimization of Laser Beam Welding Parameters for 90/10 Cupronickel Alloy Welds Using Taguchi Method

Online veröffentlicht: 09. Mai 2022

Seitenbereich: 89 - 98

DOI: https://doi.org/10.2478/scjme-2022-0009

SchlüsselwörterLaser beam welding (LBM), Copper–nickel (Cu–Ni) 90/10 alloys, Tensile strength (TS), Hardness, Design matrix and Taguchi method

© 2022 Maddili Praveena Chakravarthy et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Schlüsselwörter
Laser beam welding (LBM), Copper–nickel (Cu–Ni) 90/10 alloys, Tensile strength (TS), Hardness, Design matrix and Taguchi method