The thermodynamic behavior of 3-D orthogonal woven composite is studied to explore its structural heat transfer mechanism in a non-uniform heat load field based on finite element analysis (FEA). The temperature distribution characteristics of the resin matrix and the fabric reinforcement are observed to compare the heat absorption. Furthermore, the dynamic expansion and distribution characteristics of temperature in the 3-D orthogonal woven composite structure have also been quantitatively studied, together with simultaneously obtaining the path characteristics of the heat transfer in each system (i.e., warp yarns, weft yarns, and Z-yarns). In addition, the spatial temperature distribution characteristics of each yarn system in the fabric reinforcement are also explored. Thus, the structural mechanism of heat conduction for 3-D orthogonal woven composite is obtained.
Keywords
- 3-D orthogonal woven composite
- heat transfer
- non-uniform heat load
- finite element analysis
In recent decades, textile structural fabrics and their reinforced composite materials have been increasingly widely used in engineering due to their good mechanical properties, such as light weight and high strength. More attention has been paid to the category of this kind of materials, especially for the excellent three-dimensional (3-D) textile structural materials. The most significant feature of the 3-D textile structural fabrics is the presence of buckling and undulating yarns in the thickness direction, which makes the yarns between the adjacent layers more closely, enhances the overall load-bearing capacity of the materials, and effectively improves the mechanical performances. Therefore, this type of materials can effectively avoid the occurrence of delamination failure and enhance the damage tolerance. Using the specific processing techniques, such as vacuum-assisted resin transfer molding method (VARTM), winding method, pultrusion process, etc., the 3-D fabrics and resin can be used as the reinforcements and matrix, respectively, to manufacture the resin-based 3-D fabric reinforced composite materials, whose mechanical properties are significantly better than those of the 2-D composite materials. Since the main load-bearing parts of the composite materials are the reinforcements—that is, since the main mechanical properties of the composite materials are determined by the performance of the fabric reinforcements—the resin-based 3-D fabric reinforced composites have excellent mechanical properties, and this type of materials has been widely used in aviation aerospace, sports equipments, personal protection, transportation, and other fields [1,2,3,4,5,6].
In the field of engineering applications, composite materials will be affected not only by external mechanical loads but also by external heat load, such as the composite fan blades that have been long-term applied in high-temperature areas. In the atmospheric environment, the intrusion of heat ensures that the thermodynamic properties of composite materials are rigorously tested, and the long-term thermal-oxygen coupling effect leads to the thermal oxidative aging damage of composite materials [7, 8]. Besides, the heat is gradually transferred to the inside of the material structure through the resin matrix and fiber reinforcement, thereby generating a certain amount of thermal deformation and thermal stress. In particular, due to the difference in thermal conductivity and thermal expansion between the matrix and the fiber-reinforced body, it is easy to cause the debonding phenomenon at the interfaces between the fibers and resin, and the internal micro-cracks are also experience the initialization and propagation stages, which will inevitably greatly affect the overall mechanical properties of the composite materials [9, 10]. Therefore, studying the temperature distribution effects of the fabric-based composites in the thermal environment has important engineering significance for understanding the temperature expansion path and damage mechanism of the composite materials in the thermal fields.
At present, there are related studies on the mechanical damage of the resin-based 3-D textile structural composites in thermal fields [11,12,13]. Nevertheless, there is still a lack of in-depth study on the structural heat transfer mechanism of the 3-D orthogonal woven composites under the non-uniform thermal load. This observation holds good especially for studies dealing with the spatial temperature distribution characteristics of the main components (fiber reinforcement and resin matrix) of the fiber-reinforced composite materials in the non-uniform thermal load environment, which is of great significance for revealing the thermodynamic properties and damage mechanism of the composite materials in this category.
Furthermore, the thermodynamic behavior of composite materials under specific thermal load, conditions can be explored through the experimental analysis method. However, due to the limitations of experimental and analytical conditions, some information cannot be effectively characterized by experimental approaches, but the information is essential for in-depth understanding of the thermodynamic response and failure mechanism of composite materials. With the rapid development of computer-aided design technology, the finite element analysis (FEA) method provides a possibility to solve this problem. Thus, FEA can be employed to analyze and predict the thermodynamic behavior of fiber-reinforced composites that are subjected to heat loads. FEA has become a very powerful tool in the field of thermodynamic structure design of composites [14,15,16,17,18].
In this paper, the thermodynamic behavior of 3-D orthogonal woven composite is studied to explore its structural heat transfer mechanism in a non-uniform heat load field based on FEA. The temperature distribution characteristics of the resin matrix and the fabric reinforcement are observed to compare the heat absorption. Furthermore, the dynamic expansion and distribution characteristics of temperature in the 3-D orthogonal woven composite structure have also been quantitatively studied, and simultaneously the path characteristics of the heat transfer in each system (i.e., warp yarns, weft yarns, and Z-yarns) are obtained. In addition, the spatial temperature distribution characteristics of each yarn system in the fabric reinforcement are also explored. Thus, the structural mechanism of heat conduction for 3-D orthogonal woven composite is obtained.
Figure 1 (a) shows the typical structure of the 3-D orthogonal woven fabric. It can be seen that the buckling and undulating Z-yarn system runs through the entire thickness of the material and introduces the binding effect for the warp and weft yarn systems, which are arranged at an angle of 90° to each other, thereby forming a complete 3-D fabric structure with good structural stability.
Figure 1
The structures of 3-D orthogonal woven fabric and composite.
In addition, the 3-D orthogonal woven composite can be formed with the epoxy resin, as shown in Figure 1 (b). The raw material of the 3-D orthogonal woven fabric is glass fiber. The material parameters of yarns and resin are listed in Table 1.
Material parameters of the yarns and resin.
| Warp/Weft yarn | Glass fiber | 2.50 | 70.00 | 0.20 | 1.30 | 0.8 |
| Z-yarn | Glass fiber | 2.50 | 65.00 | 0.22 | 1.30 | 0.8 |
| Matrix | Epoxy resin | 1.05 | 3.65 | 0.40 | 0.35 | 0.9 |
The “Steady-state thermal” analysis module of the commercial finite element software ANSYS®, and Windows XP 32-bit version operating system, are used for FEA.
Figure 2 (a) shows the established finite element model of the heat conduction system of the 3-D orthogonal woven composite. Table 2 lists the relevant parameters of each component in the model.
Figure 2
Finite element model of the 3-D orthogonal woven composite subjected to the non-uniform heat load: (a) the model (unit: mm); (b) loading and boundary conditions; (c) mesh scheme (coincidence of nodes).
The related parameters of the parts in the established finite element model.
| Warp yarns | 5 | 25 |
| Weft yarns | 6 | 36 |
| Z-yarns | 1 | 6 |
| Matrix | – | 1 |
The contact, load, boundary conditions, and meshing settings for the finite element model are described below.
In the model, the contact thermal resistance between the adjacent systems is not considered, and the contact condition between the resin and each yarn system is set to “bonded” contact.
Figure 2 (b) shows the load and boundary conditions of the model. A small amount of non-uniformly distributed thermal load is applied to the central area of the upper surface of the composite material, thereby transferring heat to each component through the thermal conductivity of the medium. In addition, heat dissipation is carried out by the heat radiation effect of the different component surfaces.
The meshing result of the system is shown in Figure 2 (c). For warp, weft, and Z-yarns with the regular geometric shapes, the mesh is divided into hexahedral-based units. For the resin matrix, the tetrahedron is used to divide the mesh. In particular, for the heat-loaded area at the center of the composite surface, a significantly finer mesh is applied. The number of elements for warp yarn system, weft yarn system, Z-yarn system, and resin are 172480, 205920, 46158, and 3918, respectively.
After the resin-based textile structural composite is subjected to an external heat load, the heat first impacts the central area of the resin surface, and then the heat is transferred to the surrounding area along the transverse and longitudinal directions, respectively. In order to produce a more detailed summary of the heat transfer structural effect of the 3-D orthogonal woven composite under a kind of specific non-uniformly distributed heat load, it is necessary to explain the functions of resin, warp, weft, and Z-yarns. Figure 3 shows the temperature distribution of the above-mentioned components after the entire system reaches the steady state.
Figure 3
Temperature distribution: (a) resin; (b) fabric; (c) warp yarns; (d) weft yarns; and (c) Z-yarns.
Figure 3 (a) shows the temperature distribution on the resin matrix. It can be found that the temperature on the surface of the resin is the highest due to the direct action area of the heat load, and the highest temperature in the central area reaches 74 °C. In addition, the distribution law of the temperature gradient is consistent with the distribution state of the heat load.
The temperature distribution of the fabric reinforcement is shown in Figure 3 (b). Since the absorbed heat of the fabric reinforcement is first transferred from the resin, its maximum temperature is significantly lower than that of the resin, approximately 48 °C, which is about 65% of the maximum temperature in the resin. Therefore, considering that the heat resistance performance of the resin is much lower than that of the glass fibers, the heat-induced damage of the composite material may have first germinated from the resin. Then it mainly propagates to the internal structure along the interface between the resin and the fibers, and finally reaches the fiber reinforcement.
Furthermore, it can be observed that the highest temperature appears on the undulating Z-yarns. Since the central Z-yarn is located closest to the resin, it is the first part to be impacted by heat load, especially at the location near the direct action area of the heat load. In particular, Figure 3 (c), (d), and (e) show the respective temperature distribution characteristics of the warp yarn system, the weft yarn system, and the Z-yarn system, respectively. It can be observed that, as mentioned above, the Z-yarn system has the highest temperature, which is followed by the weft yarn system, at approximately 44 °C, and then the warp yarn system, which has the lowest temperature, whose maximum value is approximately 42 °C. It is significant that the result is closely related to the structural characteristics of the 3-D orthogonal woven fabric reinforcement of the composite.
In particular, because the Z-yarns are relatively longer and undulating, and this state runs through the entire thickness direction of the material structure, the high-temperature zone of each Z-yarn generally exists in the central area only, and the range is relatively narrow. It is difficult for the heat to propagate along the length direction. Thus, the temperature at both ends is lower. The thermal damage is generally limited to the central high-temperature area. Nevertheless, for warp and weft yarns, the situation is significantly different. Since the warp and weft yarns are arranged in a straight way without buckling, their length is relatively shorter. The central high temperature decreases steadily to the two ends, and the range is relatively wide. The low temperature at both ends is a little higher than that of the adjacent Z-yarn. Therefore, the thermal damage can easily germinate from the central area, and propagates to both ends.
In this sub-section, we explain the procedure adopted to further quantitatively explain the dynamic expansion and distribution characteristics of heat in the 3-D orthogonal woven composite structure, and then obtain the heat transfer mechanism. As shown in Figure 4 (a), we take the area where the heat load is directly applied as the center, and take the warp, weft, and thickness directions to investigate the temperature distribution in the above three paths, and the temperature distribution curve of each path is obtained, as shown in Figure 4 (b).
Figure 4
(a) The specific paths; (b) the temperature distribution curves on the specific paths.
The heat distribution characteristics of the composite can be observed when subjected to an external heat load. First, for the two directions of transverse warp and weft, the temperature distribution and change trend on these two paths are almost the same – that is, the temperature at the center of the heat load is the highest, and drops sharply in the two directions to the ends; besides, the descending speed slows down at the ends. The temperature drops from the highest at the center, where it is in the range of about 74°–33 °C; the drop is approximately 55%. Similarly, in the thickness direction, the temperature change trend is similar to those in the warp and weft directions – that is, the temperature at the starting point is the highest, and it drops sharply along the thickness direction, with a drop of approximately 55%. The above phenomenon shows that the heat dissipation performance of the 3-D orthogonal woven composite is not very good. This is closely related to the thermal conductivity capacity of each component in the composite structure – that is, the poor thermal conductivity of the component materials leads to the weak heat dissipation performance of the composite.
In order to clarify the heat transfer mechanism of the 3-D orthogonal woven composite under the non-uniform heat load, it is important to reveal the heat transfer process of each system from its specific structural characteristic.
The fabric reinforcement is the main load-carrying part of the composite, and the thermal conductivity capacity of the yarns is significantly higher than that of the resin, which is about four times that of the latter; therefore, exploring the temperature distribution characteristics of each part of the fabric reinforcement is of great significance for understanding the temperature-related structural effect of the 3-D orthogonal woven composite. As shown in Figure 5, the specific warp, weft, and Z-yarns that are closest to the directly heat load point are selected, and the temperature distribution curves along the length of each yarn are given.
Figure 5
The temperature curves along the length direction of each yarn.
It can be found that the temperature distribution on each yarn system has the obvious spatial morphology characteristics; that is, the temperature distribution along the length direction of each yarn is perceptibly affected by its spatial arrangement. In particular, this phenomenon is more pronounced on the Z-yarns. For the investigated specific warp and weft yarns, since the central region of each yarn is closest to the directly heat load area, the temperature is the highest. As mentioned above, the temperature on the weft yarn is slightly higher than that on the warp yarn. Due to the limitation of the thermal conductivity capacity of the yarns, the temperature drops sharply at both ends. For the specific Z-yarn, it has the highest temperature.
The thermodynamic behavior of 3-D orthogonal woven composite is studied to explore its structural heat transfer mechanism in a non-uniform heat load field based on FEA. By finite element modeling and analysis as well as considering the micro-structures of warp yarns, weft yarns, Z-yarns, and resin, the following conclusions have been obtained.
The temperature on the surface of the resin is the highest due to the direct action area of the heat load. Furthermore, the Z-yarn system has the highest temperature, which is followed by the weft system, and then the warp system. This result is closely related to the structural characteristics of the 3-D orthogonal woven fabric reinforcement of the composite.
For the two directions of transverse warp and weft, the temperature at the center is the highest, and it drops sharply in the two directions to the edge. The temperature drops from the highest at the center, where it is in the range of about 74°–33°C; the drop is approximately 55%. Similarly, in the thickness direction, the temperature at the starting point is the highest, and it drops sharply along the thickness direction, with a drop of approximately 55%. The above phenomenon shows that the heat dissipation performance of the 3-D orthogonal woven composite is not very good. This is closely related to the thermal conductivity capacity of each component in the composite structure.
The temperature distribution on each yarn has the obvious spatial morphology characteristics of the corresponding yarn. In particular, this phenomenon is more pronounced on the Z-yarns. Moreover, due to the limitation of the thermal conductivity capacity of the yarns, the temperature drops sharply at both ends.
For the prospects on the FEA-based thermodynamic analysis of the fiber-reinforced composite materials, the optimization design of composite materials resistant to the thermal damage can be focused on. It mainly includes the optimization for the raw materials of fibers and resin, the structural design of the reinforcement, and the fibers’ orientation. In addition, in order to ensure that the designed and manufactured composite materials have the sufficient thermodynamic properties and meet the requirements of the practical applications, the conservative calculations of FEA must be applied.
Figure 1
Figure 2
Figure 3
Figure 4
Figure 5
The related parameters of the parts in the established finite element model.
| Warp yarns | 5 | 25 |
| Weft yarns | 6 | 36 |
| Z-yarns | 1 | 6 |
| Matrix | – | 1 |
Material parameters of the yarns and resin.
| Warp/Weft yarn | Glass fiber | 2.50 | 70.00 | 0.20 | 1.30 | 0.8 |
| Z-yarn | Glass fiber | 2.50 | 65.00 | 0.22 | 1.30 | 0.8 |
| Matrix | Epoxy resin | 1.05 | 3.65 | 0.40 | 0.35 | 0.9 |
Automatic Identification Of Wrist Position In A Virtual Environment For Garment Design Pressure Evaluation Of Seamless Yoga Leggings Designed With Partition Structure Experimental and Modelling Studies on Thermal Insulation and Sound Absorption Properties of Cross-Laid Nonwoven Fabrics Tensile Properties Analysis Of 3D Flat-Knitted Inlay Fabric Reinforced Composites Using Acoustic Emission From Raw To Finished Cotton—Characterization By Interface Phenomena A Study on the Woven Construction of Fabric Dyed With Natural Indigo Dye and Finishing for Applying to Product Design for Home Textile Products A Calculation Method for the Deformation Behavior of Warp-Knitted Fabric Nondestructive Test Technology Research for Yarn Linear Density Unevenness Numerical Simulation and Analysis of Airflow in the Condensing Zone of Compact Spinning with Lattice Apron Blend Electrospinning of Poly(Ɛ-Caprolactone) and Poly(Ethylene Glycol-400) Nanofibers Loaded with Ibuprofen as a Potential Drug Delivery System for Wound Dressings Application of Plasticized Cellulose Triacetate Membranes for Recovery and Separation of Cerium(III) and Lanthanum(III) Study On Structure And Anti-Uv Properties Of Sericin Cocoons Fit And Pressure Comfort Evaluation On A Virtual Prototype Of A Tight-Fit Cycling Shirt A Fabric-Based Integrated Sensor Glove System Recognizing Hand Gesture Developing Real Avatars for the Apparel Industry and Analysing Fabric Draping in the Virtual Domain Review on Fabrication and Application of Regenerated Bombyx Mori Silk Fibroin MaterialsThe Effects of Sensory Marketing on Clothing-Buying Behavior Transport of Moisture in Car Seat Covers Review on 3D Fabrication at Nanoscale Investigation of the Performance of Cotton/Polyester Blend in Different Yarn Structures Simulations of Heat Transfer through Multilayer Protective Clothing Exposed to Flame Determination of Sewing Thread Consumption for 602, 605, and 607 Cover Stitches Using Geometrical and Multi-Linear Regression Models Polyaniline Electrospun Composite Nanofibers Reinforced with Carbon Nanotubes Effect of Surface Modification of Himalayan Nettle Fiber and Characterization of the Morphology, Physical and Mechanical Properties Investigation of Actual Phenomena and Auxiliary Ultrasonic Welding Parameters on Seam Strength of PVC-Coated Hybrid Textiles Modeling Lean and Six Sigma Integration using Deep Learning: Applied to a Clothing Company Comparative Analysis of Structure and Properties of Stereoscopic Cocoon and Flat Cocoon Effect of Different Yarn Combinations on Auxetic Properties of Plied Yarns Analysis of Heat Transfer through a Protective Clothing Package Smart Textile for Building and Living Investigation of Twist Waves Distribution along Structurally Nonuniform Yarn 3D Body Scan as Anthropometric Tool for Individualized Prosthetic Socks Preliminary Experimental Investigation of Cut-Resistant Materials: A Biomimetic Perspective Durable Wash-Resistant Antimicrobial Treatment of Knitted Fabrics Study on the Thermal and Impact Resistance Properties of Micro PA66/PU Synergistically Reinforced Multi-Layered Biaxial Weft Knitted Fabric Composites Fea-Based Structural Heat Transfer Characteristic of 3-D Orthogonal Woven Composite Subjected to the Non-Uniform Heat Load Comfort-Related Properies of Cotton Seersucker Fabrics Conductive Heat Transfer Prediction of Plain Socks in Wet State A Novel Foam Coating Approach to Produce Abrasive Structures on Textiles Textronic Solutions Used for Premature Babies: A Review Effect of Lycra Weight Percent and Loop Length on Thermo-physiological Properties of Elastic Single Jersey Knitted Fabric Texture Representation and Application of Colored Spun Fabric Using Uniform Three-Structure Descriptor Analysis of Mechanical Behavior of Different Needle Tip Shapes During Puncture of Carbon Fiber Fabric Approach to Performance Rating of Retroreflective Textile Material Considering Production Technology and Reflector Size Influence of Multilayer Interlocked Fabrics Structure on their Thermal Performance Prediction of Standard Time of the Sewing Process using a Support Vector Machine with Particle Swarm Optimization Investigation of Heat Transfer in Seersucker Woven Fabrics using Thermographic Method Comfort-Related Properties of Double-Layered Woven Car Seat Fabrics Experimental Investigation of the Wettability of Protective Glove Materials: A Biomimetic Perspective An Integrated Lean Six Sigma Approach to Modeling and Simulation: A Case Study from Clothing SME Mechanical Properties of Composites Reinforced with Technical Embroidery Made of Flax Fibers Consumer Adoption of Fast-Fashion, Differences of Perceptions, and the Role of Motivations Across the Adoption Groups Development of the Smart T-Shirt for Monitoring Thermal Status of Athletes Assessment and Semantic Categorization of Fabric Visual Texture Preferences Microscopic Analysis of Activated Sludge in Industrial Textile Wastewater Treatment Plant Application of Coating Mixture Based on Silica Aerogel to Improve Thermal Protective Performance of Fabrics A Biomimetic Approach to Protective Glove Design: Inspirations from Nature and the Structural Limitations of Living Organisms Washing Characterization of Compression Socks Estimation of Seams in Paraglider Wing Development of a Small, Covered Yarn Prototype Determination of State Variables in Textile Composite with Membrane During Complex Heat and Moisture Transport Numerical Prediction of the Heat Transfer in Air Gap of Different Garment Models Biological Properties of Knitted Fabrics Used in Post-Burn Scar Rehabilitation Fabrication and Characterization of Fibrous Polycaprolactone Blended with Natural Green Tea Extracts Using Dual Solvent Systems Archaeology and Virtual Simulation Restoration of Costumes in the Han Xizai Banquet Painting Modeling of Material Characteristics of Conventional Synthetic Fabrics